    Biogas-slurry derived mesoporous carbon for supercapacitor applications
    (Elsevier, 2017) Enock, Talam Kibona; King’ondu, Cecil K.; Pogrebnoi, Alexander; Jande, Yusufu Abeid Chande
    This study reports on the transformation of biogas slurry into mesoporous carbon for supercapacitor electrodes. Pore structures have been modified by altering activation time, temperature and KOH/carbon mass ratio. The mesoporous carbons are successively developed as evidenced by type IV isotherms obtained in nitrogen sorption studies. BET, micropore and mesopore surface area of 515, 350, and 165 m2 g−1, respectively as well as a narrow pore width distribution of 3–4.5 nm are obtained. X-ray photoelectron results have confirmed the presence of functional groups of oxygen and nitrogen in the samples which facilitates the pseudocapacitance. The electrochemical measurements in 6 M KOH using a three electrode cell with Ag/AgCl as reference electrode and platinum as counter electrode has been performed. The materials activated at 700 °C, 3:1 KOH to carbon mass ratio, and for 120 min exhibit high specific capacitance of 289 F g−1 at a scan rate of 5 mV s−1. Shortening activation time to 30 and 60 min reduces specific capacitance to 163 and 182 F g−1, in that order. Additionally, at 3:1 KOH to carbon mass ratio and 60 min activation time, specific capacitances of 170 and 210 F g−1 at 600 and 800 °C, respectively are obtained. Moreover, specific capacitance increases with increasing the KOH to carbon mass ratio from 148 F g−1 for 1:1–163 F g−1 for 3:1 at 700 °C. Electrochemical impedance spectroscopy studies demonstrate that material has high conductivity. In addition; capacity retention of 96% after 20,000 cycles is shown at scan rate of 30 mV s−1. The study shows that high performance electrodes can be designed from biogas slurry derived porous carbon.
  • Thumbnail Image
    Item
    Status of biomass derived carbon materials for supercapacitor application
    (Hindawi, 2017) Enock, Talam Kibona; King’ondu, Cecil K; Pogrebnoi, Alexander; Jande, Yusufu Abeid Chande
    Environmental concerns and energy security uncertainties associated with fossil fuels have driven the world to shift to renewable energy sources. However, most renewable energy sources with exception of hydropower are intermittent in nature and thus need storage systems. Amongst various storage systems, supercapacitors are the promising candidates for energy storage not only in renewable energies but also in hybrid vehicles and portable devices due to their high power density. Supercapacitor electrodes are almost invariably made of carbon derived from biomass. Several reviews had been focused on general carbon materials for supercapacitor electrode. This review is focused on understanding the extent to which different types of biomasses have been used as porous carbon materials for supercapacitor electrodes. It also details hydrothermal microwave assisted, ionothermal, and molten salts carbonization as techniques of synthesizing activated carbon from biomasses as well as their characteristics and their impacts on electrochemical performance.